Phosphate-activated geopolymers: advantages and application

Silica-aluminophosphate (SAP) geopolymers are a novel type of green mortar made from aluminosilicate precursors and phosphoric acid (PA), and they are attracting the interest of researchers due to their extraordinary and distinctive capabilities. According to current research, SAP geopolymers have great mechanical properties, high heat and fire resistance, and outstanding sorption activity. Because of their properties, they have a wide range of applications, including novel insulating, construction, coating, and wastewater treatment materials. This paper focuses on the most recent advances in SAP geopolymer research. Furthermore, this work indicates novel applications for SAP geopolymers, which might serve as guidance for future research activity of scientists.


Introduction
Geopolymers are three-dimensional inorganic polymeric materials constituted of cross-linked tetrahedral units [ AlO 4 ] and [SiO 4 ] and alkali metal cations.Geopolymers, a novel type of inorganic nonmetallic material with remarkable performance features, are garnering increasing interest from material scientists and technologists aer more than 40 years of research, particularly in the last 20 years.
Prof. Joseph Davidovits, a French scientist and engineer, established the name "geopolymer" in the 1970s to describe a family of solid materials formed by the interaction of an aluminosilicate powder with an alkaline solution. 1,2Following a series of res in Europe, these materials were initially developed as a re-resistant alternative to organic thermosetting polymers, and products based on this initial work have since found application as coatings for re protection for cruise ships, 3,4 as a resin in high-temperature carbon-re composites, 5,6 as a heat-resistant adhesive, 6,7 as a monolithic refractory, 8,9 and a variety of other niche applications.
Geopolymers are a subgroup of the wider class of alkaliactivated binders, 10 which also includes materials generated by alkali-, silicate-, carbonate-, or sulfate-activation of metallurgical slags, yielding mostly calcium silicate hydrate.A geopolymer is distinguished by the presence of an alkali aluminosilicate gel in the binding phase, with aluminum and silicon connected in a three-dimensional tetrahedral gel structure that is particularly resistant to dissolution in water. 11,12avidovits established the "sialate" terminology to designate aluminosilicate formations more than 40 years ago. 13Si-O-Al coupling was dubbed a sialate bond, and Si-O-Si a siloxo bond.This allowed to describe the composition of geopolymers based on their Si/Al ratio, with a ratio of 1.0 indicating a poly(sialate), 2.0 indicating a poly(sialate-siloxo), and 3.0 indicating a poly(sialate-disiloxo) (Fig. 1).
To begin with, geopolymers are a complicated class of materials.The most common way to make geopolymers is to mix an alkaline solution with a reactive aluminosilicate powder, such as metakaolin or y ash.This leads to the creation of the geopolymeric gel binder phase, a disordered alkali aluminosilicate gel phase.This phase comprises uncreated solid precursor particles, while the pore network of the gel contains the water needed to combine the precursors, which was provided via an alkaline "activating solution."The gel's fundamental framework is a highly connected three-dimensional network of aluminate and silicate tetrahedra, with the negative charge due to Al 3+ in four-fold coordination localized on one or more of the bridging oxygens in each aluminate tetrahedron and balanced by the activating solution's alkali metal cations 14 (Fig. 2).
The investigation of the area of acid activation of geopolymers, or phosphate geopolymers, has grown in prominence in recent years.Due to the change in molecular structure caused by phosphorus atoms, geopolymers activated by phosphoric or orthophosphoric acid have a variety of benets, for instance, higher thermal stability, higher mechanical strength, and higher sorption capacity.
The economic aspect might also be a crucial signal in the manufacture of geopolymer cement.Alkaline-activators, such as sodium silicate and sodium hydroxide, are frequently used in the development of appropriate materials for civil engineering applications, such as geopolymer cements.Due to the high cost of sodium silicate, this factor has a signicant impact on the nal product's pricing.As a result, phosphoric acid-based geopolymers are the ideal replacement for alkaline-based geopolymers.

Synthesis and classification
Geopolymers are formed from a reaction between an aluminosilicate precursor and an alkali or acid activator.
Alkali-activated geopolymers are formed in the presence of alkaline activators (such as NaOH and sodium silicate), and    The inclusion of contaminants such as calcium, magnesium, iron, and others inuences the composition and characteristics of these binders.For example, the presence of iron in alkaline media causes some Al to be replaced by Fe, resulting in ferroaluminosilicate gel.The inclusion of Ca 2+ in the same medium enhances the development of C-S-H forms such as tobermolite and transforms N-A-S-H gel to N-C-A-S-H. 19The presence of iron in an acidic medium causes a rapid reaction between phosphoric acid and magnetite (Fe 3 O 4 ) to generate the amorphous gels Fe(H 2 PO 4 ) 2 , Fe(H 2 PO 4 ) 3 , FeHPO 4 , and Fe 2 (HPO 4 ) 3 . 20Given the differences, the adsorption rates, adsorption capacities, and adsorption methods onto silicaaluminophosphate (SAP) and alkali-aluminosilicate (AAS) geopolymers must be different and cannot be predicted in advance.

Preparation process of geopolymers
2.1.1Raw materials.Clay minerals are an important source of aluminosilicate for the production of geopolymers. 21Metakaolin (MK), a calcination derivative of kaolinite, is oen utilized to make geopolymers due to its excellent pozzolanic characteristics. 22,23With growing concern about pollution and clean manufacturing, the utilization of industrial solid waste as raw materials for geopolymers has attracted increased attention internationally in recent years.Several solid wastes containing reactive silica and alumina, such as y ash (FA), 24 granulated blast-furnace slag, 25,26 biomass ash, 27 and red mud, 28 have been identied as promising candidate raw materials for SAP geopolymerization.
To increase pozzolanic activity, kaolinite is calcined (500-900 °C) to produce metakaolinite. 29Metakaolin is predicted to be soluble in these systems due to the existence of a signicant amorphous aluminosilicate phase that dissolves easily in sodium hydroxide solutions. 30ecause of their consolidation effect, tailings are frequently utilized as a raw material for concrete or cement, particularly heavy-metal-contaminated tailings. 31Acid-based geopolymers, in the contrary, have better bonding and consequently higher compressive strengths than alkali-based geopolymers. 32hang et al. (2020) 33 synthesized geopolymer using the spent uid catalytic-cracking (SFCC) catalyst instead of metakaolin, and the material's highest compressive strength was 41.22 MPa.Bouzón et al. (2014) 34 combined the SFCC catalyst and rice husk ash to produce geopolymers.The compressive strength of geopolymer was found to be between 31 and 41 MPa.However, the authors employed alkali-activation of geopolymers in these investigations, whereas Wan et al. (2022) 35 used SFCC catalyst as a raw material for the formation of phosphate geopolymers with a maximum compressive strength of 30.2 MPa.
Fly ash is a form of industrial solid waste made mostly of CaO, Al 2 O 3 , and SiO 2 by coal-red power plants.Fly ash (FA) is oen classied as high-calcium y ash (HCFA) or low-calcium y ash (LCFA) based on its CaO level.Wang et al. (2020) 36 investigated the micromorphology and geopolymerization mechanisms of HCFA and LCFA.Fig. 3 represents SEM images of HCFA and LCFA, setting time of samples, elemental mapping and compressive strength results.Further investigations suggest that adding solid wastes such as blast furnace slag and electrolytic manganese slag may speed up the geopolymerization procedure, and the resulting geopolymer samples have good water resistance and high temperature resistance. 25,26able 1 shows the various kinds and constituents of precursors employed in the synthesis of SAP geopolymers.
The principal mineral is kaolinite, which is commonly combined with quartz, anatase, and illite.It can also be linked with goethite, hematite, gibbsite, and halloysite, depending on the geological context.Some studies looked at the effect of secondary minerals found in kaolin on the qualities of geopolymer cements hardened using sodium silicate.The effects of halloysite in kaolin on the characteristics of geopolymer materials were explored by Zhang et al. (2012). 46studied the effect of gibbsite in kaolin on the characteristics of metakaolin-phosphate-based geopolymer cements.They discovered that a larger gibbsite concentration in kaolin had a detrimental effect on the characteristics of the resulting geopolymer cements.
From all the aforementioned, it can be noted that the constitution of raw materials used in the preparation process of SAP geopolymers plays a crucial role due to the complex mechanism of formation.For SAP geopolymers, the major component must be Al 2 O 3 , because the formation of tetrahedral bonds is established by the reaction between Al 3+ and PO 4 3− groups.
Different minerals contained in the starting material can also change the properties of geopolymers, which is why it is necessary to know the mineralogical content of the raw material.Regarding the studies, the best properties were observed with quartz, halloysite, illite, and anatase, whereas gibbsite and hematite have a negative effect on the mechanical properties of SAP geopolymers.
2.1.2Curing conditions.In SAP production, the curing temperature is a crucial component that greatly affects the geopolymer's properties and curing time.SAP does not solidify and harden as quickly as AAS does at room temperature because of the delayed release of silicon and aluminum in aluminosilicate in acidic media.The metakaolin (MK) and H 3 PO 4 solution frequently takes an excessively long time (more than 48 h) to set at room temperature, 50 so SAP samples are frequently created at higher curing temperatures.The optimal curing temperature of SAP for constant temperature curing was found to be 70 °C, and higher curing temperatures were detrimental to SAP's properties. 43 multi-stage curing process is more frequently used to create SAP geopolymers, in which the mixes are typically precured at high temperatures of 50-90 °C for up to 2 days, followed by a lengthy curing at room temperature.40,[51][52][53] Lin et al.
(2021) 54 created SAP geopolymers using a two-stage curing process and found that the higher curing temperature caused signicant cracking in the SAP samples due to the rapid exothermic reaction and expansive stress caused by the high internal temperature rise.The SAP samples with the highest compressive strength of 123.4 MPa were produced using a two-  °C yields the greatest improvement and higher pore size (Fig. 5).When compared to diluted phosphoric acid-containing soluble aluminum, the curing temperature is the most favorable parameter for quickening the reaction kinetic.This is because heat promotes not only the dissolving of aluminum from volcanic ash, but also the solubility of other reactive components such as iron, calcium, magnesium, and, to a smaller extent, silicon.
The Therefore, it can be concluded that curing conditions can change the compressive strength of SAP geopolymers obtained from different starting materials.The best way to prepare SAP geopolymers with desired mechanical properties is to use a twostage curing method, comprising low-temperature treatment at the rst stage (40-50 °C) for 24-48 hours, and high-temperature treatment at the second stage (60-80 °C) for 24-48 hours.
2.1.3Concentration of activating solution.The concentration of the activating solution, such as phosphoric acid (PA), plays an important role in the synthesis of SAP geopolymers.SAP compressive strengths are generally modest aer activation with low concentration PA.This was due to the polymerization reaction necessitating a greater acid dosage and curing temperature in order to achieve a high rate of Si and Al dissolving from precursor particles, which could subsequently polymerize into a three-dimensional network structure as the load bearing structure. 56he principal reaction products in phosphate-based geopolymer, according to Wang et al. (2017), 57 were an amorphous structure of SiO 2 $Al 2 O 3 $P 2 O 5 $nH 2 O and a crystalline phase, aluminum hydrogen phosphate (AlH 3 (PO 4 )$3H 2 O), which resulted in improved strength.Using 6.8 mol L −1 PA-activated FA, Pu et al. created SAP with compressive strengths ranging from 3 to 21 MPa. 58Mahyar et al. (2015), 59 on the other hand, used 8.7 mol L −1 PA-activated FA to generate SAP with compressive strengths ranging from 15 to 22 MPa.As a result, increasing the concentration of PA does not always improve the mechanical characteristics of SAP.Furthermore, high PA concentrations generated signicant amounts of heat during the polymerization procedure, reducing the setting of SAP, which is harmful to engineering applications and increases costs. 56,60In recent study, He et al. (2023) 61 prepared SAP with FA and acid solutions with concentrations of 1, 2, 3, 4 mol L −1 .They conclude that compressive strength of samples increased by 24.44% when the PA concentration was increased from 1 to 4 mol L −1 (Fig. 6).
Wan et al. (2022) 35 investigated whether the concentration of phosphoric solutions has a signicant effect on the mechanical properties of geopolymer synthesized with the SFCC catalyst using the SFCC catalyst as an aluminosilicate precursor and acid solutions with concentrations of 6, 8, 10, 12, and 14 mol L −1 .When the acid content was between 6 and 12 mol L −1 , a stable binder with a compressive strength ranging from 9.8 to 30.2 MPa was prepared (Fig. 7).A greater acid content can increase raw material dissolution and the development of geopolymer gels.
Accordingly, the concentration of activating solution sharply affects the compressive strength of SAP geopolymers.The low   concentration of acid solution, approximately 2-4 mol L −1 , showed the least compressive strength, whereas the samples obtained with acid solution concentrations of 6-14 mol L −1 showed good mechanical strength.This is because with low concentrations of acid solutions, there is a small number of PO 4  3− ions that can bond aluminum from the raw material, which leads to the least formation of [AlPO 4 ] tetrahedrals and thus low mechanical strength.

Geopolymerization mechanism of phosphategeopolymers
Zribi and Baklouti, 52,56 proposed the formation mechanism of SAP geopolymers, regarding which the geopolymerization process can be divided into three main steps and illustrated as follows (Fig. 8): (1) The rst stage is dealumination of the aluminosilicate precursor process.This phase is demonstrated to take place within the rst 30 minutes of the examined synthesis setting.The procedure is further divided into two basic parts.The rst assault attacks all Al-O-Al bonds, but the second is selective and only targets a subset of Si-O-Al bonds.
(2) As the second phase, condensation is carried out.This process is divided into four parts based on the chemical makeup of the reactant units and the resulting units: the synthesis of silicate aluminum phosphate phases, aluminum phosphate phases, silicate phosphate phases, and amorphous silica phases.This stage occurs at a varied rate from the beginning of the reaction until 12 hours have passed.In reality, as the reaction time increases, this pace reduces and becomes practically constant aer 12 hours.
(3) The third stage is polycondensation.This stage begins during the rst hour of the response and continues at a sluggish rate for several days.As a result, various 3D polymerized networks are formed.

Thermal stability
Recent research has revealed that SAP geopolymers have high heat stability, which AAS geopolymers and ordinary Portland cement (OPC) do not have.According to Liu et al. (2012), 62 ASP geopolymers show excellent thermal stabilities at 1550 °C, whereas OPC would peel off or even rupture within at high temperatures.This is because geopolymer crystallizes at high temperatures to generate quarts, cristobalite, and aluminum phosphate, which provide exceptional thermal stability to geopolymer concretes.Celerier et al.
(2018) 63 discovered that the heat resistance of ASP geopolymers is dependent on the starting material, such as metakaolin, and its composition.Furthermore, the author stated testing at high temperatures several compositions that endured re, implying that they did not become brittle following the treatment.Fig. 9 shows the compositions of water and re-resistant geopolymers.
Thermal resistant geopolymer ceramics have potential uses such as furnace refractory boards, casting mold cores, reretardant concrete, runway pavement, and so on.These applications necessitate strong thermal and mechanical qualities.These applications need strong temperature resistance as well as adequate mechanical qualities.However, conventional geopolymer materials lack mechanical strength as well as heat resistance.Fiber reinforcing is recognized as an effective approach for improving ceramics' mechanical and thermal resistance.To improve the characteristics of geopolymers, a variety of bers are used as reinforcing phases, including natural bers such as cotton ber, 64 wood ber, 65 hemp ber, 66 and others. 67,68examined the thermal characteristics of SAP modied with mullite bers and discovered that mullite ber has a high affinity for phosphate geopolymer and has a considerable ber reinforcing effect.As shown in the Fig. 10, despite the presence of microcracks on the surface of the obtained samples, modied geopolymers demonstrated remarkable thermal stability at 1350 °C, however at temperatures over 1450 °C, geopolymers began to breakdown owing to AlPO 4 melting.
In consequence, SAP geopolymers have gained a potential number of applications in the heat and re resistance materials area due to their high thermal stability.This property depends on the mineralogical constitution of the raw materials used in the preparation process and the transformation of minerals under high-temperature treatment.Moreover, the reinforcement of SAP geopolymers with mullite bers and silicon carbide bers also increases the heat resistance of geopolymer concrete.

Thermal insulation
Thermal insulation is dened as the decrease of heat transfer between objects in thermal contact or within the range of controlled radiative. 73Thermal insulating material can be dened as a single substance or mixture of materials that, when appropriately applied, slows the rate of heat transport by conduction, convection, and radiation.Because of its high thermal resistance, it slows heat movement into or out of an object or structure. 74Thermal insulation can be done by the use of properly designed technologies or processes, as well as appropriate object forms and materials.Thermal insulation creates an insulating area in which thermal conduction is decreased or thermal radiation is reected rather than absorbed by the lower-temperature substance.Thermal insulating materials impede heat ow as a result of innumerable tiny dead air-cells that inhibit convective heat transmission.The thermal resistance is provided by the air trapped within the insulation, not by the insulation material itself.Making holes or tiny cells within thermal insulation with a slight temperature differential decreases radiation impact.It breaks down radiation "paths" into short lengths where longwave infrared radiation is absorbed and dispersed by the insulating material. 74norganic materials (glass, rock, slag wool, ceramic goods, geopolymers) and organic materials (cellulose, cotton, wood, foamed rubber, polystyrene, polyethylene, polyurethane) are examples of acceptable thermal insulation materials.However, geopolymers have been used to create more effective insulating materials.SAP geopolymers have been studied as thermal insulation materials by several researchers and have received a lot of interest due to their remarkable heat insulating capabilities.
Chen et al. (2020) 76 created a Daytime Radiative Cooling (DRC) coating using SAP geopolymers.In order to create a strong phosphate geopolymer (PGEO) covering, they employed metakaolinite as a starting material and a mixture of phosphoric acid and aluminum hydroxide as an activating solution.In the solar irradiation band, the produced PGEO covering with a thickness of 50 mm exhibits almost 90% reectance.Under direct sunlight, the coating's exceptional spectrum selectivity results in a subambient temperature reduction at the coated surface of up to 8.3 °C.Furthermore, the spectrum selectivity of the PGEO coating was maintained across a variety of extreme environmental conditions, including high temperature, mechanical abrasion, and proton irradiation (Fig. 11).As a result, this PGEO covering has prospective applications in solar-exposed components such as spacecra and buildings.geopolymers.The thermal conductivity of the tested samples ranged from 0.09 to 0.43 W m −1 K −1 .Fig. 12 depicts a facility for assessing thermal conductivity, SEM pictures of samples, and compressive strength of samples.
Rashad et al. (2023) 88 manufactured SAP geopolymers from metakaolin using sugar beet waste as a foaming agent and investigated the thermal insulation capabilities of the resulting samples.As a result of applying 6% foaming agent, the lowest thermal conductivity of the produced geopolymers was 0.08 W m −1 K −1 .This value is signicantly lower than that of other alkaline-activated insulating materials.They also evaluated the thermal conductivity of typical insulating materials and found that geopolymers foamed with sugar beet waste may be employed in large-scale thermal insulation applications.
Jouin et al. (2023) 89 created SAP geopolymers out of metakaolin and compared their thermal conductivity with the properties of other insulating materials.They reviewed the literature and determined that SAP geopolymers may be utilized in the building of insulating applications, as well as in the eld of refractories to lighten bricks and for ltering.
Hence, SAP geopolymers have least thermal and radioactive conductivity due to their morphology and porous structure.Regarding the mentioned research, SAP geopolymers have found their application in different areas, for instance, as daytime radiative cooling coatings in spacecra and construction and as excellent heat insulating materials widely used in construction.

Porosity and porous foam materials
At the present time, the production of SAP geopolymer porous foam materials by adding foaming agents is a sufficient direction in the SAP geopolymer application study.SAP geopolymer porous foam materials are not only heat and re resistant but also light weight, heat insulation, and have a high sorption capacity, making them a possible novel type of thermal insulation material and adsorbents. 62Aluminum powder, 60,80 iron powder, 80 surfactant, 81 hydrogen peroxide, 82 and limestone 77,78 are now applied as foaming agents.
The fundamental concepts for creating SAP geopolymer foams may be separated into two groups.One method is to apply foaming agents such as aluminum/iron powder or limestone to react with alkali or acid to create gas, which results in a homogeneous and rich foam structure when the geopolymer paste is formed.The alternative option is to employ a surfactant-based foaming agent that is directly combined with the slurry.
Porous geopolymers may be produced from metakaolin and H 3 PO 4 using aluminum powder as a foaming agent, according to Le-ping et al. (2010). 60The porosity of the foamed geopolymer samples ranged from 40% to 83%, with compressive strength ranging from 7 to 13 MPa.
Shuai et al. (2019) 82 created SAP foamed geopolymers from metakaolin and foamed them with hydrogen peroxide solutions at concentrations of 2, 2.5, 3, 3.5, and 4%.The porosity of the produced samples ranged from 55% to 64%, with the greatest compressive strength achieved at 4% and 2% H 2 O 2 solutions.Bai et al. (2019) 81 used the surfactant Triton X-100 as a foaming agent in the preparation process of SAP geopolymer foam material from metakaolin.The obtained geopolymers showed high mechanical strength, re resistance, and porosity.They reported that geopolymers foamed with surfactant are ecofriendly and can be used in construction.
Morsy et al. (2019) 78 combined metakaolin with limestone to produce foamed SAP geopolymers.As a result of their research, they obtained highly porous geopolymers with low thermal conductivity and reasonable mechanical strength.
Yang et al. (2023) 83 used both aluminum powder and hydrogen peroxide as foaming agents with a combination of high magnesium nickel slag (HMNS) and y ash (FA) as starting material.As a result, they have obtained porous materials with a low dry density and low thermal conductivity.For geopolymers foamed with H 2 O 2 , the results of thermal conductivity were higher than for samples foamed with Al.However, for water absorption tests, samples foamed with Al showed the highest result compared to samples foamed with H 2 O 2 (Fig. 13).They also concluded that HMNS-FA foamed SAP geopolymers can be used as thermal insulation materials and as water storage materials.
Rashad et al. (2023) 88 employed carbonated lime residue (CR), a waste product of the sugar beet production sector, as a foaming agent in the synthesis of metakaolin-based porous geopolymers.As a consequence, they concluded that CR can be used as a foaming agent since the foamed geopolymers generated had low heat conductivity and reasonable compressive strength.The collected samples have a total porosity of 61.2% and a bulk density of 631.5 kg m −3 .
According to the mentioned studies, SAP geopolymers can be easily foamed with different types of foaming agents, starting with aluminum powder and ending with surfactants.Moreover, foamed SAP geopolymers have great mechanical properties, the lowest thermal conductivity, and high adsorption properties, which gives them a wide range of applications in different areas.

Adsorption properties
Adsorption is recognized as one of the most successful wastewater treatment strategies due to the availability of a variety of adsorbent materials that are inexpensive in cost, readily available, and can be manufactured utilizing a simple step of synthesis.
Previous research has demonstrated that SAP geopolymers have good adsorption and solidication properties for heavy metals and radioactive nuclear waste. 84Phosphate-based geopolymers can effectively prevent heavy metal ion or radioactive element leaching by rmly blocking heavy metal ions in the cavity of their unique three-dimensional network structure.
Khan et al. (2015) 85 investigated phosphate-based geopolymers for wastewater treatment by removing methylene blue (MB) from water using SAP geopolymers.As a result, SAP geopolymers easily absorbed MB from water, according to their ndings.Furthermore, geopolymers are thermally stable and may be regenerated several times without compromising adsorption capabilities.Njimou et al. 86 investigated the removal of Pb(II) ions from aqueous solutions using a SAP geopolymer-alginate composite.The resulting SAP geopolymer-alginate composite (Alg/CES) beads had an adsorption capacity of 0.183 mmol g −1 , a pH of 4.27, and an initial concentration of 113.4 mg L −1 .They determined that such geopolymer composite is environmentally benign and suited for heavy metals wastewater treatment.
Liu et al. (2022) 90 tested the adsorption of combinations of Pb(II), Cd(II), and Ni(II) using foamed SAP geopolymer.Metakaolin was used to create geopolymers, which were then foamed with H 2 O 2 and stabilized with Triton X-100.As a consequence, they discovered that the pH of the solution plays an important role in heavy metal adsorption, with pH 7 providing the best adsorption effectiveness for heavy metal ions (Fig. 15).Furthermore, they compared the sorption performance of SAP geopolymers to that of AAS geopolymers and found that the sorption performance of SAP geopolymers is much greater than that of AAS geopolymers.
Therefore, SAP geopolymers have gained huge attention in wastewater treatment applications because of their microstructure and morphology.Geopolymers are able to immobilize heavy metal ions inside their three-dimensional network structure, which is necessary in current ecological conditions.SAP geopolymers can be widely used in production due to the fact that their results on sorption capacity and leaching tests exceed those of AAS geopolymers.

Durability
One of the most crucial characteristics required in the development of geopolymer applications is durability.Water resistance is the most important feature in geopolymer engineering application index.
According to Mimboe et al. (2020), 91 the strength loss of SAP geopolymer based on laterite soaking in water for 24 h surpasses 60% of dry compressive strength.Ndjock study (2021) 92 discovered that SAP geopolymers immersed in water for 24 hours had a 54% loss in compressive strength, whereas Nobouassia et al. (2018) 93 discovered a 54% decrease in compressive strength aer soaking in water for 28 days.
However, the endurance of SAP geopolymers can be enhanced by adding a Ca source, such as slags.According to Djobo and Stephan et al. (2021), 94 geopolymers made with pozzolanic ash lowered the strength loss rate from 40.3% to 24.7%.7 investigated the water resistance capabilities of produced binders using FA as the raw material for SAP geopolymer samples.Samples were soaked for 7, 28, 180, and 270 days.As a consequence, samples submerged for 7 and 28 days lost 40% of their strength, whereas samples soaked for 180 days had no visible fractures on their surface.However, aer soaking for 280 days, the samples grew fragile and began to break (Fig. 16).Therefore, the main issue with SAP geopolymers in their current state is durability.According to previous studies, SAP geopolymer binders have a decrease in compressive strength of 40-60%.However, depending on the constitution of the raw material used for the preparation process of SAP geopolymers, the loss of compressive strength can be decreased.However, this area of study needs to be studied more because durability is one of the major factors in the production of construction materials.

Possible applications in the future
According to the investigations, SAP geopolymers have numerous benecial characteristics, including strong compressive strength, 51 good heat resistance, 71,72 and high sorption activity. 85,86,90However, there are certain impending concerns with SAP geopolymers, such as a long polycondensation time at room temperature, and low water and corrosion resistance.As a result, we can forecast the potential application direction of SAP geopolymers in the future based on their strengths and negative aspects.
SAP geopolymers' outstanding mechanical qualities and heat resistance, when compared to other commonly used construction materials, allow them to be employed in construction and building materials.However, the fact that SAP geopolymers can solidify quicker only at increased temperatures, about 60-80 °C, might be mentioned as a major limitation in SAP geopolymer manufacture.As a result, raising the temperature during binder curing increases expenses as well as CO 2 gas pollution.A further weakness of SAP geopolymers is their low water endurance, which leads to material failure.As an outcome of all the research reviewed, there are just two main drawbacks that merit further investigation.For example, the endurance of SAP geopolymers can be extended by adding certain components to the binder or by employing starting materials with high calcium or iron oxide constitutions, which give greater water resistance.As a result, all problems in SAP geopolymers may be overcome, and there are many more benets than we can anticipate.
A prior investigation has shown that SAP geopolymers may be formed as foams featuring good heat resistance, low thermal conductivity, and good water adsorption, and can be used as a lightweight insulation material. 83Furthermore, SAP geopolymers with high hardness, spectrum selectivity, and adhesion can be used as daytime radiative cooling coatings in urban construction and spacecra. 76Furthermore, SAP geopolymers have strong heavy metal adsorption characteristics, making them promising materials for wastewater treatment. 85,86,90rom all aforementioned, despite minor difficulties that may be resolved, we believe SAP geopolymers have a bright future in the construction industry.

Conclusion
This study analyzes the most recent advances in silicoaluminophosphate (SAP) geopolymer production, categorization, characteristics, and applications.SAP geopolymers have superior mechanical qualities, high heat and re resistance, low thermal conductivity, and strong sorption activity, according to the present research.These features make SAP geopolymers green building materials with a wide range of applications in insulating materials, coating materials, and wastewater treatment.Thoroughly minimizing the issue of curing conditions and enhancing the durability of SAP geopolymers would aid in the promotion of SAP geopolymer industrialization applications.

Fig. 2
Fig. 2 (a) Proposed model for the location of the charge-balancing Na + cation which assumes the form of a semi attached Na aluminate species; (b) proposed model for the location of the charge-balancing Na + cation which assumes the form of a modified bridging network; (c) proposed schematic model for alkali-activated geopolymer structure based on an original model.This figure has been adapted/reproduced from ref. 14 with permission from Springer Nature under the license number 5632330146683, copyright 2023.

Fig. 3
Fig. 3 (1) SEM image of LCFA; (2) SEM image of HCFA; (3) typical backscattered electron images and elemental mapping results of the H30 geopolymer after 28 days curing; (4) initial and final setting time of the SAP geopolymers with different types and contents of CFA; (5) compressive strength results of the FA-SAP geopolymers with different types and contents of FA.This figure has been adapted/reproduced from ref. 36 with permission from Elsevier under the license number 5632320548892, copyright 2023.

Fig. 4 ( 1 )
Fig. 4 (1) appearance of the SAP samples: (a) cured at 60 °C, (b) cured by the two-stage curing method (pre-cured at 40 °C for 24 h, then cured at 60 °C/80 °C for 24 h); (2) setting time of the SAPs cured at different temperatures; (3) images of the SAP samples obtained after the two-step curing at 60 °C: (a) SAP1 with low P/Al molar ratio of 0.52, (b) SAP2-SAP4 with relatively high P/Al ratios of 0.64-0.84;(4) development of compressive strength of the SAPs in the second curing stage (a) cured at 60 °C, (b) cured at 80 °C.This figure has been adapted/reproduced from ref. 54 with permission from Elsevier under the license number 5632321036081, copyright 2023.
opposite results were obtained by Bewa et al. (2019). 55They used calcined laterite as an aluminosilicate source to explore the impact of curing temperature on the characteristics of phosphate-based geopolymers.The acid-based geopolymers were cured for 24 hours at room temperature, 40, 50, 60, 70, 80, and 90 °C.In comparison to specimens cured at 40-90 °C, whose highest compressive strength was in the range of 24.0-65 MPa, they discovered that specimens treated at room temperature had compressive strength values of 83.0 MPa or higher.

Fig. 6
Fig. 6 Compressive strength of SAP (L/Fliquid to fly ash ratio; PAphosphoric acid).This figure has been adapted/reproduced from ref. 61 with permission from Elsevier under the license number 5630021114812, copyright 2023.

Fig. 8
Fig. 8 Conceptual model of the proposed formation mechanism of phosphate based geopolymers.This figure has been adapted/reproduced from ref. 56 with permission from Elsevier under the license number 5630020882161, copyright 2023.

Fig. 10
Fig. 10 SEM images of samples treated at different temperatures, Wei et al., Materials, 2022. 72 Fig. 11 (1) Photographs showing the mechanical linear abrasion test performed on sandpaper (standard glasspaper, grit no.240) with 100 g of abrading load; (2) comparison of the thickness reduction of the PGEO and the organic DRC coatings at different linear abrasion distances; (3) SEM surface morphology of the coating after an abrasion distance of 50 cm; (4) comparison of the adhesive strength of the PGEO coating and the organic DRC coating to an Al substrate; (5) measured solar spectral reflectance of the PGEO coating compared to that of the organic DRC coating before (dashed lines) and after (solid lines) space proton irradiation; (6) overall comparison of performance for the as-prepared PGEO coating, photonic crystals, and organic polymer radiative cooling designs.This figure has been adapted/reproduced from ref. 76 with permission from American Chemical Society, copyright 2023.

Fig. 12 ( 1 )
Fig. 12 (1) Scheme of facility for measuring thermal conductivity; (2) the structure of the cleavage of composite No. (1) Fired at 1000 °C a -filler and bbinder; (3) effect of filler content on the properties of composite ceramics based on perlite, heat-treated at 1000 °C; (1) density.(2) Compressive strength.This figure has been adapted/reproduced from ref. 79 with permission from Elsevier under the license number 5630030100032, copyright 2023.

Fig. 15 ( 1 )
Fig. 15 (1) Removal efficiency of Pb, Ni and Cd by PAG (SAP) from single, binary and ternary mixtures; (2) effect of pH on the removal efficiency, equilibrium pH; (3) metal adsorption amount of Pb, Ni and Cd by PAG (SAP) in ternary mixtures; (4) possible mechanism of heavy metals adsorption by phosphoric acid-based geopolymer.This figure has been adapted/reproduced from ref. 90 with permission from Elsevier under the license number 5630030483481, copyright 2023.
Kaze et al. (2021) 96 created SAP geopolymer binder using iron-rich laterite.As a consequence, they determined that the iron oxide composition of SAP geopolymers boosts durability and creates stronger water resistance than AlP geopolymers.Pu et al. (2022)

Fig. 16
Fig.16 Evolution of geopolymer specimens different soaking times, Pu et al., Dev.Built Environ., 2022.97 Rüscher et al. (2013) 47 investigated the impact of quartz content in raw materials on the development of compressive strength in geopolymer cements.Essaidi et al. (2014) 48 looked into the role of hematite in metakaolin aluminosilicate gels.They observed that the inclusion of iron oxide affects the synthesis of geopolymer compounds, resulting in the development of consolidated materials with the lowest compressive strength values.They stated that the compressive strengths of the collected specimens ranged from 4.0 to 27.0 MPa.Tchakouté et al. (2017)